鸿图工程PA66 日本东洋纺织 T-663GN30 玻纤30％填充-中国工控网(chinagkong.com)-中国工控行业门户网站

首页 > 供应 > 工程塑料 >

鸿图工程PA66 日本东洋纺织 T-663GN30 玻纤30％填充

来自：东莞鸿图工程塑胶

26人民币

发布时间：2012-11-5 关注次数：203

产品参数

商品详情

[ T-663G30(GF30%) ]

Classification					GF reinforced
Classification					Nylon66
Properties			Test method ASTM	Unit	T-663G30 (GF30%)
Properties			Test method ASTM	Unit	Absolute drying	Practical use (Water absorption 1.75%)
Physical properties	Filler content rate		%		30	−
	Specific Gravity		D-792	−	1.37	−
	Hardness		D-785	R scale	121	−
	Water absorption	23, 24hr. in water	D-570	%	0.6	−
	Water absorption	65%R.H. equilibrium	D-570	%	1.7	−
Mechanical properties	Tensile strength	-40	D-638	MPa	235	215
		23			195	145
		80			120	100
	Tensile elongation	23	D-638	%	3.2	3.9
	Flexural strength	-40	D-790	MPa	315	300
		23			280	210
		80			185	130
	Flexural modulus	-40	D-790	GPa	10.8	9.8
		23			8.7	5.8
		80			5.4	4.0
	IZOD notched impact test	-40	D-256	J/m	70	80
	IZOD notched impact test	23	D-256	J/m	110	140
	Compression strength	23	D-695	MPa	−	−
	Taber abrasion	CS-17 1000cycles	D-1044	mg/1000turns	−	−
Thermal properties	Cofficient of linear thermal expansion		D-696	10^-5/K	−	−
	Deflection temperature under load	0.46MPa	D-648		262	−
	Deflection temperature under load	1.82MPa	D-648		255	−
	Thermal Index		UL-94	class/mm	HB class
Electric properties	Dielectric strength	2mmt	D-149	MV/m	26	20
	Volume Resistivity		D-257	Ω•m	10¹³	10^10-11
	Dielectric constant	1kHz	D-150	1kHz	4.1	−
	Dielectric disspation factor	1kHz	D-150	1kHz	−	−
	Arc resistance		D-495	sec.	100	92
	Comparation Tracking Index		IEC Method	CTI	575	575
Molding condition	Melt flow Index			g/10min	7	−
	Resine temperature				280-310	−
	Mold temperature				60 ~	−
	Injection pressure			MPa	30-60	−
	Mold shrinkage	1mm thickness		%	0.2-0.5	−
	Mold shrinkage	3mm thickness		%	0.6-0.9	−