INCOFLUXR NT100 埋弧焊剂

INCOFLUX NT100 埋弧焊剂是一种中性的烧结焊剂，设计与Nickel 61、INCONEL82、NI-ROD 44和NILO CF36 焊丝匹配使用。这种焊剂的典型应用是Nickel200合金自身之间或与钢之间的开坡口焊接，以及与INCONEL 61匹配使用在碳钢表面进行堆焊。这种焊剂也可以与INCONEL 82填充金属相匹配，形成多达三层的堆焊层。（注意，如果需要更多的堆焊层，应当使用INCOFLUX 4埋弧焊剂INCONEL 82填充金属）。NI-ROD 44填充金属和INCOFLUX NT100 埋弧焊剂匹配可以用于铸铁之间以及铸铁和钢之间的埋弧焊接。INCOFLUX NT100 埋弧焊剂也可以与NILO CF36填充金属匹配用于INVAR合金和NILO 36合金的焊接。

储藏和干燥条件

焊剂密封在未开启的容器中可以无限期保存。如果焊剂暴露于潮湿环境中，可以在500^oF保温烘干2小时或600^oF保温烘干1小时后使用。

The INCOFLUX NT100 submerged arc welding agent is a neutral sintering flux, designed with Nickel 61, INCONEL82, ni-rod 44 and NILO CF36 welding wire. The typical application of such flux is the weld between the Nickel200 alloy itself or the open groove between the steel, and the INCONEL 61 matching for surfacing welding on the surface of carbon steel. The flux can also be matched with the INCONEL 82 filler metal, forming up to three layers of surfacing. (note that INCOFLUX 4 submerged arc welding agent INCONEL 82 filler metal should be used if more surfacing layers are needed. NI-ROD 44 filler metal and INCOFLUX NT100 submerged arc welding can be used for the submerged arc welding between cast iron and steel and steel. The INCOFLUX NT100 submerged arc welding agent can also be used to match the NILO CF36 filler metal for the welding of the INVAR alloy and the NILO 36 alloy.

Welding parameters: open groove welding or surfacing: apply DCEP current and narrow weld path

Electrode dry extension flux layer thickness of wire diameter current/ampere voltage/v welding speed electrode

Nickel 61

0.062 in

The 1.6 mm

250

28 and 30

10-12 in/min

The 250-305 - mm/min

In 7/8-1

22 to 25 mm

In 1/2-1

13 to 25 mm

0.093 in

2.4mm 250-300 30-33 8-11 in/min

In 200-280 - mm/min 7/8-1

22-25 mm 3/4-5/4 in

19 to 32 mm

Electrode swing surfacing welding: the use of DCEN current mode, when the wire diameter is 0.062 in, the oscillation frequency is 50-70 weeks/min; When the wire diameter is 0.093 in, the oscillation frequency is 35-50 weeks/min

0.062 in

1.6 mm 240-2632-34 4 in/min

100 mm/min in 7/8-1

1/2-1 in 22 to 25 mm

13 to 25 mm

0.093 in

2.4mm 300-400 34-37 4 in/min

100 mm/min in 7/8-1

22-25 mm 3/4-5/4 in

19 to 32 mm

Storage and drying conditions

The flux seals can be kept indefinitely in unopened containers. If the solder is exposed to wet conditions, it can be used after an hour of thermal insulation drying for 2 hours or 600oF.

Flux particle size

Taylor's mesh: 10 times 100

packaging

The barrel cover is covered with a 50 pound polyethylene barrel sealed with rubber gasket